Alloy 6005
is similar to alloy 6061 When produced to a -T5 temper, it has the same minimum tensile and yield strength as 6061-T6 and better machinability and strength properties than 6063-T6. Alloy 6005A may also replace 6061 due to its better extrudability and surface appearance.
6005 aluminum alloy
is the most commonly used on foreign vehicles, extrusion performance and comprehensive performance of the better aluminum.
6005 aluminum plate is Al-Mg alloy, is the most widely used a rust-proof aluminum.
The alloy is used in a wide range and is the most promising alloy.
Aluminum 6005 aluminum has the following advantages:
1, good corrosion resistance, excellent weldability, cold workability is better, and with moderate strength;
2, high strength, especially with anti-fatigue strength, plasticity and high corrosion resistance;
3, good forming processing performance;
6005 PLATE SPECIFICATIONS
| Alloys | Tempers | thickness(mm) | width(mm) | length(mm) | Typical products |
| 6005 | O, T4, T6, T651 | 0.3-600 | 300-1600 | 800-6000 | Aircraft fuel tank / tubing, transportation vehicles / ship's sheet metal pieces |
Typical applications for 6005A alloy include:
| 97.5 to 99 | ||
| 0.6 to 0.9 | ||
| 0.4 to 0.6 | ||
| 0 to 0.35 | ||
| 0 to 0.1 | ||
| 0 to 0.1 | ||
| 0 to 0.1 | ||
| 0 to 0.1 | ||
| 0 to 0.1 | ||
| 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.