5052 O Temper Aluminum Round Bar Rod Used In Marine Applications
Magnesium is the primary alloying agent in the 5052 series and is one of the most effective and widely used alloying elements for aluminum. Alloys in this series possess moderate to high strength characteristics, as well as good weldablilityand resistance to corrosion in the marine environment. Because of this, aluminum-magnesium alloys are widely used in building and construction, storage tanks, pressure vessels and marine applications.
| Mechanical Properties | ||||
| ||||
| Hardness, Brinell | 47 | 47 | AA; Typical; 500 g load; 10 mm ball | |
| Ultimate Tensile Strength | 193 MPa | 28000 psi | AA; Typical | |
| Tensile Yield Strength | 89.6 MPa | 13000 psi | AA; Typical | |
| Elongation at Break | 25 % | 25 % | AA; Typical; 1/16 in. (1.6 mm) Thickness | |
| Elongation at Break | 30 % | 30 % | AA; Typical; 1/2 in. (12.7 mm) Diameter | |
| Modulus of Elasticity | 70.3 GPa | 10200 ksi | AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus. | |
| Ultimate Bearing Strength | 345 MPa | 50000 psi | Edge distance/pin diameter = 2.0 |
| Bearing Yield Strength | 131 MPa | 19000 psi | Edge distance/pin diameter = 2.0 |
| Poisson's Ratio | 0.33 | 0.33 | |
| Fatigue Strength | 110 MPa | 16000 psi | AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen |
| Machinability | 30 % | 30 % | 0-100 Scale of Aluminum Alloys |
| Shear Modulus | 25.9 GPa | 3760 ksi | |
| Shear Strength | 124 MPa | 18000 psi | AA; Typica |